Each sample groups how it was prepared, characterized, and measured. Click a card to expand.
2 preparations3 characterizations8 properties2 figures
1 preparation2 characterizations2 figures
2 characterizations2 figures
| Type | Label | Value | Material | Sample | Condition | Source |
|---|---|---|---|---|---|---|
| Fet Threshold Voltage | peak responsivity gate bias | 0.5V | — | |||
| Fet Mobility | responsivity at 406 nm | 0.19A/W | — | |||
| Fet Mobility | responsivity at 642 nm | 0.32A/W | — | |||
| Fet Mobility | responsivity at 785 nm | 0.18A/W | — | |||
| Fet Mobility | rise time | 0.3s | — | |||
| Fet Mobility | fall time | 1.7s | — | |||
| Fet Mobility | rise time upper bound | 1.1s | — | |||
| Fet Mobility | fall time upper bound | 2.1s | — | |||
| Raman Peak | regex-detected Raman peak | 2665cm⁻¹ | — | — | — | — |
| Raman Peak | regex-detected Raman peak | 2688cm⁻¹ | — | — | — | — |
| Raman Peak | regex-detected Raman peak | 1582cm⁻¹ | — | — | — | — |
| Raman Peak | regex-detected Raman peak | 1588cm⁻¹ | — | — | — | — |
| Raman Peak | regex-detected Raman peak | 1339cm⁻¹ | — | — | — | — |
| Raman Peak | regex-detected Raman peak | 1347cm⁻¹ | — | — | — | — |
| Raman Peak | regex-detected Raman peak | 1583cm⁻¹ | — | — | — | — |
| Raman Peak | regex-detected Raman peak | 2620cm⁻¹ | — | — | — | — |
| Raman Peak | regex-detected Raman peak | 1353cm⁻¹ | — | — | — | — |
| Raman Peak | regex-detected Raman peak | 1575cm⁻¹ | — | — | — | — |
| Raman Peak | regex-detected Raman peak | 2220cm⁻¹ | — | — | — | — |
| Ir Band Position | IR band | 1575cm⁻¹ | — | — | — | — |
| Ir Band Position | IR band | 2220cm⁻¹ | — | — | — | — |
| Ir Band Position | aromatic C=C | 1400cm⁻¹ | — | — | — | — |
| Ir Band Position | epoxy C-O-C | 900cm⁻¹ | — | — | — | — |
Related documents with shared materials, methods, properties, or citations.
Cross-Dimensional Exciton Coupling in Quantum Dot–Carbon Nanotube Hybrid Thin Films
Observation of Ultrafast Interfacial Exciton Formation and Recombination in Graphene/MoS2 Heterostructure
Electrodeposition of amorphous molybdenum sulfo-selenide as a low-cost catalyst
Hexagonal boron nitride nanophotonics
Cove-Edged Chiral Graphene Nanoribbons with Chirality-Dependent Bandgap and Carrier Mobility
Electroluminescence of the graphene 2D semi-metal
Resonance Raman scattering and anomalous anti-Stokes phenomena in CrSBr
Gate-tunable quantum acoustoelectric transport in graphene
A quasi-ohmic back contact achieved by inserting single-crystal graphene in flexible Kesterite solar cells
Each sample groups how it was prepared, characterized, and measured. Click a card to expand.
2 preparations3 characterizations8 properties2 figures
1 preparation2 characterizations2 figures
2 characterizations2 figures
| Type | Label | Value | Material | Sample | Condition | Source |
|---|---|---|---|---|---|---|
| Fet Threshold Voltage | peak responsivity gate bias | 0.5V | — | |||
| Fet Mobility | responsivity at 406 nm | 0.19A/W | — | |||
| Fet Mobility | responsivity at 642 nm | 0.32A/W | — | |||
| Fet Mobility | responsivity at 785 nm | 0.18A/W | — | |||
| Fet Mobility | rise time | 0.3s | — | |||
| Fet Mobility | fall time | 1.7s | — | |||
| Fet Mobility | rise time upper bound | 1.1s | — | |||
| Fet Mobility | fall time upper bound | 2.1s | — | |||
| Raman Peak | regex-detected Raman peak | 2665cm⁻¹ | — | — | — | — |
| Raman Peak | regex-detected Raman peak | 2688cm⁻¹ | — | — | — | — |
| Raman Peak | regex-detected Raman peak | 1582cm⁻¹ | — | — | — | — |
| Raman Peak | regex-detected Raman peak | 1588cm⁻¹ | — | — | — | — |
| Raman Peak | regex-detected Raman peak | 1339cm⁻¹ | — | — | — | — |
| Raman Peak | regex-detected Raman peak | 1347cm⁻¹ | — | — | — | — |
| Raman Peak | regex-detected Raman peak | 1583cm⁻¹ | — | — | — | — |
| Raman Peak | regex-detected Raman peak | 2620cm⁻¹ | — | — | — | — |
| Raman Peak | regex-detected Raman peak | 1353cm⁻¹ | — | — | — | — |
| Raman Peak | regex-detected Raman peak | 1575cm⁻¹ | — | — | — | — |
| Raman Peak | regex-detected Raman peak | 2220cm⁻¹ | — | — | — | — |
| Ir Band Position | IR band | 1575cm⁻¹ | — | — | — | — |
| Ir Band Position | IR band | 2220cm⁻¹ | — | — | — | — |
| Ir Band Position | aromatic C=C | 1400cm⁻¹ | — | — | — | — |
| Ir Band Position | epoxy C-O-C | 900cm⁻¹ | — | — | — | — |
Related documents with shared materials, methods, properties, or citations.
Cross-Dimensional Exciton Coupling in Quantum Dot–Carbon Nanotube Hybrid Thin Films
Observation of Ultrafast Interfacial Exciton Formation and Recombination in Graphene/MoS2 Heterostructure
Electrodeposition of amorphous molybdenum sulfo-selenide as a low-cost catalyst
Hexagonal boron nitride nanophotonics
Cove-Edged Chiral Graphene Nanoribbons with Chirality-Dependent Bandgap and Carrier Mobility
Electroluminescence of the graphene 2D semi-metal
Resonance Raman scattering and anomalous anti-Stokes phenomena in CrSBr
Gate-tunable quantum acoustoelectric transport in graphene
A quasi-ohmic back contact achieved by inserting single-crystal graphene in flexible Kesterite solar cells
Each sample groups how it was prepared, characterized, and measured. Click a card to expand.
2 preparations3 characterizations8 properties2 figures
1 preparation2 characterizations2 figures
2 characterizations2 figures
| Type | Label | Value | Material | Sample | Condition | Source |
|---|---|---|---|---|---|---|
| Fet Threshold Voltage | peak responsivity gate bias | 0.5V | — | |||
| Fet Mobility | responsivity at 406 nm | 0.19A/W | — | |||
| Fet Mobility | responsivity at 642 nm | 0.32A/W | — | |||
| Fet Mobility | responsivity at 785 nm | 0.18A/W | — | |||
| Fet Mobility | rise time | 0.3s | — | |||
| Fet Mobility | fall time | 1.7s | — | |||
| Fet Mobility | rise time upper bound | 1.1s | — | |||
| Fet Mobility | fall time upper bound | 2.1s | — | |||
| Raman Peak | regex-detected Raman peak | 2665cm⁻¹ | — | — | — | — |
| Raman Peak | regex-detected Raman peak | 2688cm⁻¹ | — | — | — | — |
| Raman Peak | regex-detected Raman peak | 1582cm⁻¹ | — | — | — | — |
| Raman Peak | regex-detected Raman peak | 1588cm⁻¹ | — | — | — | — |
| Raman Peak | regex-detected Raman peak | 1339cm⁻¹ | — | — | — | — |
| Raman Peak | regex-detected Raman peak | 1347cm⁻¹ | — | — | — | — |
| Raman Peak | regex-detected Raman peak | 1583cm⁻¹ | — | — | — | — |
| Raman Peak | regex-detected Raman peak | 2620cm⁻¹ | — | — | — | — |
| Raman Peak | regex-detected Raman peak | 1353cm⁻¹ | — | — | — | — |
| Raman Peak | regex-detected Raman peak | 1575cm⁻¹ | — | — | — | — |
| Raman Peak | regex-detected Raman peak | 2220cm⁻¹ | — | — | — | — |
| Ir Band Position | IR band | 1575cm⁻¹ | — | — | — | — |
| Ir Band Position | IR band | 2220cm⁻¹ | — | — | — | — |
| Ir Band Position | aromatic C=C | 1400cm⁻¹ | — | — | — | — |
| Ir Band Position | epoxy C-O-C | 900cm⁻¹ | — | — | — | — |
Related documents with shared materials, methods, properties, or citations.
Cross-Dimensional Exciton Coupling in Quantum Dot–Carbon Nanotube Hybrid Thin Films
Observation of Ultrafast Interfacial Exciton Formation and Recombination in Graphene/MoS2 Heterostructure
Electrodeposition of amorphous molybdenum sulfo-selenide as a low-cost catalyst
Hexagonal boron nitride nanophotonics
Cove-Edged Chiral Graphene Nanoribbons with Chirality-Dependent Bandgap and Carrier Mobility
Electroluminescence of the graphene 2D semi-metal
Resonance Raman scattering and anomalous anti-Stokes phenomena in CrSBr
Gate-tunable quantum acoustoelectric transport in graphene
A quasi-ohmic back contact achieved by inserting single-crystal graphene in flexible Kesterite solar cells
Each sample groups how it was prepared, characterized, and measured. Click a card to expand.
2 preparations3 characterizations8 properties2 figures
1 preparation2 characterizations2 figures
2 characterizations2 figures
| Type | Label | Value | Material | Sample | Condition | Source |
|---|---|---|---|---|---|---|
| Fet Threshold Voltage | peak responsivity gate bias | 0.5V | — | |||
| Fet Mobility | responsivity at 406 nm | 0.19A/W | — | |||
| Fet Mobility | responsivity at 642 nm | 0.32A/W | — | |||
| Fet Mobility | responsivity at 785 nm | 0.18A/W | — | |||
| Fet Mobility | rise time | 0.3s | — | |||
| Fet Mobility | fall time | 1.7s | — | |||
| Fet Mobility | rise time upper bound | 1.1s | — | |||
| Fet Mobility | fall time upper bound | 2.1s | — | |||
| Raman Peak | regex-detected Raman peak | 2665cm⁻¹ | — | — | — | — |
| Raman Peak | regex-detected Raman peak | 2688cm⁻¹ | — | — | — | — |
| Raman Peak | regex-detected Raman peak | 1582cm⁻¹ | — | — | — | — |
| Raman Peak | regex-detected Raman peak | 1588cm⁻¹ | — | — | — | — |
| Raman Peak | regex-detected Raman peak | 1339cm⁻¹ | — | — | — | — |
| Raman Peak | regex-detected Raman peak | 1347cm⁻¹ | — | — | — | — |
| Raman Peak | regex-detected Raman peak | 1583cm⁻¹ | — | — | — | — |
| Raman Peak | regex-detected Raman peak | 2620cm⁻¹ | — | — | — | — |
| Raman Peak | regex-detected Raman peak | 1353cm⁻¹ | — | — | — | — |
| Raman Peak | regex-detected Raman peak | 1575cm⁻¹ | — | — | — | — |
| Raman Peak | regex-detected Raman peak | 2220cm⁻¹ | — | — | — | — |
| Ir Band Position | IR band | 1575cm⁻¹ | — | — | — | — |
| Ir Band Position | IR band | 2220cm⁻¹ | — | — | — | — |
| Ir Band Position | aromatic C=C | 1400cm⁻¹ | — | — | — | — |
| Ir Band Position | epoxy C-O-C | 900cm⁻¹ | — | — | — | — |
Related documents with shared materials, methods, properties, or citations.
Cross-Dimensional Exciton Coupling in Quantum Dot–Carbon Nanotube Hybrid Thin Films
Observation of Ultrafast Interfacial Exciton Formation and Recombination in Graphene/MoS2 Heterostructure
Electrodeposition of amorphous molybdenum sulfo-selenide as a low-cost catalyst
Hexagonal boron nitride nanophotonics
Cove-Edged Chiral Graphene Nanoribbons with Chirality-Dependent Bandgap and Carrier Mobility
Electroluminescence of the graphene 2D semi-metal
Resonance Raman scattering and anomalous anti-Stokes phenomena in CrSBr
Gate-tunable quantum acoustoelectric transport in graphene
A quasi-ohmic back contact achieved by inserting single-crystal graphene in flexible Kesterite solar cells
figure_digitization.json#Figure 5figure_digitization.json#Figure S2(a)figure_digitization.json#Figure S2(b)figure_digitization.json#Figure S4figure_digitization.json#Figure 5figure_digitization.json#Figure S2(a)figure_digitization.json#Figure S2(b)figure_digitization.json#Figure S4figure_digitization.json#Figure 5figure_digitization.json#Figure S2(a)figure_digitization.json#Figure S2(b)figure_digitization.json#Figure S4figure_digitization.json#Figure 5figure_digitization.json#Figure S2(a)figure_digitization.json#Figure S2(b)figure_digitization.json#Figure S4