Abstract

We measure the two-dimensional elastic modulus E₂D of atomically clean defect-engineered graphene with a known defect distribution and density in correlated ultra-high vacuum experiments. The vacancies are introduced via low-energy (< 200 eV) Ar ion irradiation and the atomic structure is obtained via semi-autonomous scanning transmission electron microscopy and image analysis. Based on atomic force microscopy nanoindentation measurements, a decrease of E₂D from 286 to 158 N/m is observed when measuring the same graphene membrane before and after an ion irradiation-induced vacancy density of 1.0 × 10¹³ cm⁻². This decrease is significantly greater than what is predicted by most theoretical studies and in stark contrast to some measurements presented in the literature. With the assistance of atomistic simulations, we show that this softening is mostly due to corrugations caused by local strain at vacancies with two or more missing atoms, while the influence of single vacancies is negligible. We further demonstrate that the opposite effect can be measured when surface contamination is not removed before defect engineering.

Abstract

We measure the two-dimensional elastic modulus E₂D of atomically clean defect-engineered graphene with a known defect distribution and density in correlated ultra-high vacuum experiments. The vacancies are introduced via low-energy (< 200 eV) Ar ion irradiation and the atomic structure is obtained via semi-autonomous scanning transmission electron microscopy and image analysis. Based on atomic force microscopy nanoindentation measurements, a decrease of E₂D from 286 to 158 N/m is observed when measuring the same graphene membrane before and after an ion irradiation-induced vacancy density of 1.0 × 10¹³ cm⁻². This decrease is significantly greater than what is predicted by most theoretical studies and in stark contrast to some measurements presented in the literature. With the assistance of atomistic simulations, we show that this softening is mostly due to corrugations caused by local strain at vacancies with two or more missing atoms, while the influence of single vacancies is negligible. We further demonstrate that the opposite effect can be measured when surface contamination is not removed before defect engineering.

Abstract

We measure the two-dimensional elastic modulus E₂D of atomically clean defect-engineered graphene with a known defect distribution and density in correlated ultra-high vacuum experiments. The vacancies are introduced via low-energy (< 200 eV) Ar ion irradiation and the atomic structure is obtained via semi-autonomous scanning transmission electron microscopy and image analysis. Based on atomic force microscopy nanoindentation measurements, a decrease of E₂D from 286 to 158 N/m is observed when measuring the same graphene membrane before and after an ion irradiation-induced vacancy density of 1.0 × 10¹³ cm⁻². This decrease is significantly greater than what is predicted by most theoretical studies and in stark contrast to some measurements presented in the literature. With the assistance of atomistic simulations, we show that this softening is mostly due to corrugations caused by local strain at vacancies with two or more missing atoms, while the influence of single vacancies is negligible. We further demonstrate that the opposite effect can be measured when surface contamination is not removed before defect engineering.

Abstract

We measure the two-dimensional elastic modulus E₂D of atomically clean defect-engineered graphene with a known defect distribution and density in correlated ultra-high vacuum experiments. The vacancies are introduced via low-energy (< 200 eV) Ar ion irradiation and the atomic structure is obtained via semi-autonomous scanning transmission electron microscopy and image analysis. Based on atomic force microscopy nanoindentation measurements, a decrease of E₂D from 286 to 158 N/m is observed when measuring the same graphene membrane before and after an ion irradiation-induced vacancy density of 1.0 × 10¹³ cm⁻². This decrease is significantly greater than what is predicted by most theoretical studies and in stark contrast to some measurements presented in the literature. With the assistance of atomistic simulations, we show that this softening is mostly due to corrugations caused by local strain at vacancies with two or more missing atoms, while the influence of single vacancies is negligible. We further demonstrate that the opposite effect can be measured when surface contamination is not removed before defect engineering.