Research paper
Experimental CharacterizationTheoreticalCoherent spectroscopy of a single Mn-doped InGaAs quantum dot
J. Filipovic, A. Kundu, N. K. Vij, S. F´echerolle et al.
Copyright © 2026 Matter42. All rights reserved.
| Type | Label | Value | Material | Sample | Condition | Source |
|---|---|---|---|---|---|---|
| PL Peak | X+ emission manifold | 1.336eV | — | |||
| PL Peak | splitting Δ between |1⟩→|4⟩ and |3⟩→|4⟩ transitions | 750µeV | — | |||
| Pl Peak Fwhm | resonance FWHM | 17µeV | — | |||
| Pl Peak Fwhm | natural linewidth | 0.8µeV | — | |||
| PL Peak | non-resonant excitation laser | 1.95eV | — |
| Type | Label | Value | Material | Sample | Condition | Source |
|---|---|---|---|---|---|---|
| PL Peak | X+ emission manifold | 1.336eV | — | |||
| PL Peak | splitting Δ between |1⟩→|4⟩ and |3⟩→|4⟩ transitions | 750µeV | — | |||
| Pl Peak Fwhm | resonance FWHM | 17µeV | — | |||
| Pl Peak Fwhm | natural linewidth | 0.8µeV | — | |||
| PL Peak | non-resonant excitation laser | 1.95eV | — |
| Type | Label | Value | Material | Sample | Condition | Source |
|---|---|---|---|---|---|---|
| PL Peak | X+ emission manifold | 1.336eV | — | |||
| PL Peak | splitting Δ between |1⟩→|4⟩ and |3⟩→|4⟩ transitions | 750µeV | — | |||
| Pl Peak Fwhm | resonance FWHM | 17µeV | — | |||
| Pl Peak Fwhm | natural linewidth | 0.8µeV | — | |||
| PL Peak | non-resonant excitation laser | 1.95eV | — |
| Type | Label | Value | Material | Sample | Condition | Source |
|---|---|---|---|---|---|---|
| PL Peak | X+ emission manifold | 1.336eV | — | |||
| PL Peak | splitting Δ between |1⟩→|4⟩ and |3⟩→|4⟩ transitions | 750µeV | — | |||
| Pl Peak Fwhm | resonance FWHM | 17µeV | — | |||
| Pl Peak Fwhm | natural linewidth | 0.8µeV | — | |||
| PL Peak | non-resonant excitation laser | 1.95eV | — |
figure_digitization.json#Figure 2(a)figure_digitization.json#Figure 2(b)figure_digitization.json#Figure 2(c)figure_digitization.json#Figure 2(d)figure_digitization.json#Figure 3(a)figure_digitization.json#Figure 3(sub)figure_digitization.json#Figure 4(b)figure_digitization.json#Figure 4(c)figure_digitization.json#Figure 4(d)figure_digitization.json#Figure 4(e)figure_digitization.json#Figure 4(f)figure_digitization.json#Figure 5figure_digitization.json#Figure 5figure_digitization.json#Figure 2(a)figure_digitization.json#Figure 2(b)figure_digitization.json#Figure 2(c)figure_digitization.json#Figure 2(d)figure_digitization.json#Figure 3(a)figure_digitization.json#Figure 3(sub)figure_digitization.json#Figure 4(b)figure_digitization.json#Figure 4(c)figure_digitization.json#Figure 4(d)figure_digitization.json#Figure 4(e)figure_digitization.json#Figure 4(f)figure_digitization.json#Figure 5figure_digitization.json#Figure 5figure_digitization.json#Figure 2(a)figure_digitization.json#Figure 2(b)figure_digitization.json#Figure 2(c)figure_digitization.json#Figure 2(d)figure_digitization.json#Figure 3(a)figure_digitization.json#Figure 3(sub)figure_digitization.json#Figure 4(b)figure_digitization.json#Figure 4(c)figure_digitization.json#Figure 4(d)figure_digitization.json#Figure 4(e)figure_digitization.json#Figure 4(f)figure_digitization.json#Figure 5figure_digitization.json#Figure 5figure_digitization.json#Figure 2(a)figure_digitization.json#Figure 2(b)figure_digitization.json#Figure 2(c)figure_digitization.json#Figure 2(d)figure_digitization.json#Figure 3(a)figure_digitization.json#Figure 3(sub)figure_digitization.json#Figure 4(b)figure_digitization.json#Figure 4(c)figure_digitization.json#Figure 4(d)figure_digitization.json#Figure 4(e)figure_digitization.json#Figure 4(f)figure_digitization.json#Figure 5figure_digitization.json#Figure 5